PFA原料日本大金AP-210
熔指14，流动性好
通用料，耐应力开裂性好，强度和电气性能好。
应用于：复杂注塑件，电线绝缘，管材
NEOFLON PFA是四氟乙烯和全氟烷基乙烯基醚的共聚物。它是一种全氟聚合物，仅由碳原子和氟原子组成，没有任何氢原子。它具有与PTFE相同的性能，适用范围从极低到高温。此外，它具有的透明度，高温下的机械强度。它可以用与普通热塑性树脂相同的模塑方法模塑而成。具有良好的熔体流动性。适合注塑成型
NEOFLON™ AP-210
Perfluoroalkoxy
DAIKIN AMERICA, INC.
产品说明：
NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.
NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 2.14 到 2.16 | g/cm³ | ASTM D792 |
| 表观密度 | 1.00 到 1.40 | g/cm³ | JIS K6891 |
| 熔流率（熔体流动速率） (372°C/5.0 kg) | 10 到 17 | g/10 min | ASTM D1238 |
| 吸水率 (饱和) | < 0.010 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 60 到 70 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (屈服) | 25.4 到 30.4 | MPa | JIS K6891 |
| 伸长率 (断裂) | 350 到 450 | % | JIS K6891 |
| 弯曲模量 | 580 到 690 | MPa | ASTM D790 |
| 压缩模量 | 490 到 590 | MPa | ASTM D695 |
| 压缩强度 | ASTM D695 | ||
| 1% 应变 | 4.90 到 5.90 | MPa | ASTM D695 |
| 25% 应变 | 31.4 到 33.3 | MPa | ASTM D695 |
| 摩擦系数 (与钢 - 静态) | 0.040 到 0.050 | ||
| 负载变形 | ASTM D621 | ||
| 25°C, 14 MPa 1 | 8.00 到 9.00 | % | ASTM D621 |
| 25°C, 14 MPa 2 | 2.50 到 3.00 | % | ASTM D621 |
| 100°C, 6.9 MPa 3 | 8.50 到 9.50 | % | ASTM D621 |
| 100°C, 6.9 MPa 4 | 2.00 到 3.00 | % | ASTM D621 |
| Flexural Strength | No break | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 无断裂 | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融温度 | 300 到 310 | °C | ASTM D4591 |
| 线形热膨胀系数 - 流动 (20 到 100°C) | 1.2E-4 | cm/cm/°C | ASTM D696 |
| 比热 | 1050 | J/kg/°C | |
| 导热系数 | 0.26 | W/m/K | ASTM C177 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 (1.57 mm) | V-0 | UL 94 | |
| 极限氧指数 (1.57 mm) | > 95 | % | ASTM D2863 |
| 充模分析 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体粘度 (380°C) | 2.00E+6 到 2.50E+7 | mPa·s |
聚四氟乙烯（PTFE）
普通PTFE管是白色不透明的，主要有导管、软管、管道内衬管、编织增强管等。PTFE管具有优异的耐高低温性能和卓越的耐化学药品性，可以输送温度高达260℃的液体或气体，而且化学纯度高，适于宽范围的连续工作温度的要求。PTFE 管优异的电性能也使其成为电子、电工领域适宜的材料，主要用于电工绝缘护套、化工输送、热交换器、医用尿路导管和手术用血管旁路。
2、四氟乙烯—全氟烷氧基乙烯基醚共聚物(PFA)
PFA物理性能、电性能和化学性能与聚四氟乙烯类似
3/二者主要的区别是PFA 是可熔融加工的热塑性塑料。PFA管具有优异的耐应力开裂性和弯曲寿命，但是渗透性能不如PTFE。PFA 管金属离子含量很低，并且在较高的温度下能够保持较强的机械强度和爆破压力。其化学纯度符合FDA要求，耐温高达260℃。