TPO-聚烯烃热塑性弹性体ThermoplasticPolyolefin：烯烃类TPE系以PP为硬链段和EPDM为软链段的共混物，简称TPO。由于它比其它TPE的比重轻(仅为0.88)，耐热性高达100℃，耐天侯性和耐臭氧性也好，因而成为TPE中又一发展很快的品种。TPV-动态硫化热塑性弹性体：1973年出现了动态部分硫化的TPO，特别是在1981年美国Mansanto公司开发成功以Santoprere命名的完全动态硫化型的TPO之后
THERMOLAST® K TC6GPZ (Series: GP/FG)
Thermoplastic Elastomer
KRAIBURG TPE
产品说明：
The GP/FG Series is your material solution for a variety of different applications.It is particularly appropriate for passenger compartments. The compounds are available in natural and black colors.
Typical applications
Car mats
Function and design elements
Handles (tools, toolboxes, skipoles)
Seals
Soft touch surface (thumb wheels, push buttons, switches)
Material advantages
Adhesion to PP
Easy coloring (compounds in natural colors)
Excellent mechanical properties
Excellent processing behavior
Fulfills specifications for automotive interior
Pleasant surface feel (Soft touch)
UL 94 HB listed
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.10 | g/cm³ | ISO 1183 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 59 | ISO 7619 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 1(屈服) | 8.00 | MPa | ISO 37 |
| 伸长率 2(断裂) | 750 | % | ISO 37 |
| 撕裂强度 3 | 16 | kN/m | ISO 34-1 |
| 压缩**变形 4 | ISO 815 | ||
| 23°C, 72 hr | 21 | % | ISO 815 |
| 70°C, 24 hr | 34 | % | ISO 815 |
| 100°C, 24 hr | 68 | % | ISO 815 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 | HB | UL 94 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 60.0 到 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 料筒1区温度 | 160 | °C | |
| 料筒2区温度 | 180 | °C | |
| 料筒3区温度 | 200 | °C | |
| 口模温度 | 200 到 230 | °C |
TPE弹性体具有优越的物理、化学性能且易于加工，同时，该产品还具有无毒、无污染并可回收二次加工的环保优势。因此，在众多工业领域被广泛应用，如：玩具、运动器材、鞋材、文具、五金、电动工具、通讯、电子产品、食品和饮料包装、家用电器、厨房用品、医疗器械、汽车、建筑工程、电线电缆等。