Plexiglas 6NPlexiglas 7HPlexiglas 7MPlexiglas 7NPlexiglas 8HPlexiglas 8NPlexiglas Heatresist FT15Plexiglas Heatresist hw55Plexiglas Heatstop 8N blackPlexiglas Hi-Gloss NTA-1Plexiglas Hi-Gloss NTA-3Plexiglas LED 8N LD12Plexiglas LED 8N LD24Plexiglas LED 8N LD48Plexiglas LED 8N LD96Plexiglas LED white 0V200Plexiglas LED white 0V606Plexiglas Optical PO Optical PO Optical PO Resist zk20Plexiglas Resist zk30Plexiglas Resist zk40Plexiglas Resist zk4BRPlexiglas Resist zk4HCPlexiglas Resist zk50Plexiglas Resist zk5BRPlexiglas Resist zk5HCPlexiglas Resist zk5HFPlexiglas Resist zk6BRPlexiglas Resist zk6HCPlexiglas Resist zk6HFPlexiglas Satinice df20 8NPlexiglas Satinice df21 8NPlexiglas Satinice df22 7HPlexiglas Satinice df22 7NPlexiglas Satinice df22 8NPlexiglas Satinice df22 zk6BRPlexiglas Satinice df23 7HPlexiglas Satinice df23 7NPlexiglas Satinice df23 8NPlexiglas Satinice df23 zk6BRPlexiglas Satinice df33 7H
亚克力PMMA无明显熔点，160°开始软化，180°可以流动，分解温度为270°。注塑温度的可调区间比较大。注塑时，一般使用温度为180℃--240℃；它吸少量水分，生产时，需烘干。先分析一下气泡形成的原因：内部有气泡无外乎两种情况：1，塑料收缩，当注塑压力保压压力不适当时，制品密度不够高，材料在收缩过程中，因温度冷却是由外至内的，内部更容易被收缩成空洞形成状似气泡的东西。2，注塑螺杆中的气体被填充进模具型腔时，这股气体不能排出型腔聚集在材料内部。产生气体的原因一般有:1,料温过高或高温下储料时间过长，材料发生气化产生气体。2，塑料中的添加剂一般耐温较低，在高温下首先发生分解气化。3，原料干燥不够，含有水分，水分气化。
所以，按上述的适合的温度加工，降低料温，提高模温，降低注塑速度，增加保压压力，延长烘料时间这些措施都可以改善气泡的问题。